Brittle dental ceramics: A challenge in dentistry.

The challenge of dental ceramic degradation necessitates innovative technology, rigorous testing and proactive dental care, demanding collaboration between researchers, dentists and patients to ensure durable and reliable dental restorations.

Influence of ceramic crown design (translucent monolithic zirconia vs. bilayered) of implant-supported single crowns after mechanical cycling.

OBJECTIVES: This study aimed to assess the influence of translucent monolithic versus bilayered crowns and whether the use of a CoCr base abutments affects the fatigue and fracture resistance of screwed implant-supported single crowns with external connections under mechanical cycling. MATERIALS AND METHODS: Fifty specimens were divided into groups: (1) metal-ceramic (MC) crown, (2) veneered zirconia crown (Zr), (3) veneered zirconia crown with a CoCr base abutment (ZrB), (4) monolithic translucent zirconia crown (MZr), and (5) monolithic translucent zirconia crown with a CoCr base abutment (MZrB). Specimens underwent mechanical cycling (5 × 106 cycles; 150 N) evaluating fatigue resistance (number of failures) and those that failed were subsequently subjected to fractographic analyses (stereomicroscope and scanning electron microscope) to evaluate failure location and area, and maximum fracture load was also measured. RESULTS: The failure-related survival rate (100%) and maximum fracture resistance of the MZrB were significantly higher than those of MC and Zr (50%; p < 0.05). There were no significant differences in the failure rate and fracture resistance when a CoCr base abutment was used or not in the translucent monolithic Zr groups (p > 0.05;MZrB vs. MZr). Failure location, with MC crowns' fractures, noted at the screw area (p = 0.043), while all-ceramic crowns were mostly in the cuspid and to failure area, the Zr group had the largest mean (15.55 ± 9.17 mm2) among the groups, significant difference only when compared with MC (1.62 ± 0.81 mm2) (p = 0.025). CONCLUSIONS: Translucent monolithic zirconia crowns exhibited significantly higher fatigue and fracture resistance compared with conventional MC and bilayered crowns. CLINICAL SIGNIFICANCE: The appropriate choice of material and manufacturing technique is crucial for predicting the higher clinical performance of single crowns. Enhanced mechanical resistance in terms of fatigue and fracture resistance can be achieved by replacing MC and bilayered restorations with computer-aided design and computer-aided manufacturing monolithic zirconia.

Clinical outcomes of self-glazed zirconia veneers produced by 3D gel deposition: a retrospective study.

BACKGROUND: Self-glazed zirconia (SZ) restorations are made by a novel additive three-dimensional gel deposition approach, which are suitable for a straightforward completely digital workflow. SZ has recently been used as minimally invasive veneer, but its clinical outcomes have not been clarified yet. This study aimed to evaluate the preliminary clinical outcomes of SZ veneers compared with the widely used lithium disilicate glass-ceramic veneers made by either pressing (PG) or milling (MG) process. METHODS: Fifty-six patients treated with SZ, PG, and MG veneers by 2 specialists between June 2018 and October 2022 were identified. Patients were recalled for follow-up at least 1 year after restoration. Clinical outcomes were assessed by 2 independent evaluators according to the modified United States Public Health Service (USPHS) criteria. Overall patient satisfaction was assessed using visual analogue scale (VAS), and analyzed by one-way ANOVA. Chi-square test was applied to compare the difference in the success and survival rates among the 3 groups. RESULTS: A total of 51 patients restored with 45 SZ, 40 PG, and 41 MG veneers completed the study, with a patient dropout rate of 8.9%. Mean and standard deviation of follow-up period was 35.0 ± 14.7 months. All restorations performed well at baseline, except for 2 SZ veneers with mismatched color (rated Bravo). During follow-up, marginal discrepancy (rated Bravo) was found in 4 MG veneers and 1 PG veneer, and partially fractured (rated Charlie) was found in another 2 PG veneers. The survival rate of SZ, PG, and MG veneers was 100%, 95%, and 100%, with a success rate of 95.56%, 92.50%, and 90.24%, respectively, none of which were significantly different (p = 0.099 and 0.628, respectively). The mean VAS score of SZ, PG, and MG was 95.00 ± 1.57, 93.93 ± 2.40, and 94.89 ± 2.00 respectively, without significant difference (p > 0.05). CONCLUSION: SZ veneers exhibited comparable preliminary clinical outcomes to PG and MG veneers, which could be considered as a feasible option for minimally invasive restorative treatment.

Synthesis of Organopolysilazane Nanoparticles as Lithium-Ion Battery Anodes with Superior Electrochemical Performance via the Two-Step Stöber Method.

The Stöber method, a widely utilized sol-gel technique, stands as a green and reliable approach for preparing nanostructures on a large scale. In this study, we employed an enhanced Stöber method to synthesize organopolysilazane nanoparticles (OPSZ NPs), utilizing polysilazane oligomers as the primary precursor material and ammonia as the catalytic agent. By implementing a two-step addition process, control over crucial parameters facilitated the regulation of the nanoparticle size. Generally, maintaining relatively low concentrations of organopolysilazane and catalyst while adjusting the water/acetonitrile ratio can effectively enhance the surface energy of the organopolysilazane, resulting in the uniform formation of small spherical particles. The average particle size of the synthesized OPSZ NPs is about 140 nm, which were monodispersed and characterized by scanning electron microscopy, transmission electron microscopy, and dynamic light scattering. Furthermore, the composition of OPSZ NPs after pyrolysis was confirmed as SiC2.054N0.206O1.631 with 5.44 wt % free carbon structure by X-ray diffraction and energy-dispersive X-ray spectroscopy. Notably, the electrochemical performance assessment of SiCNO NPs as potential electrode materials for lithium-ion batteries exhibited promising outcomes. Specifically, at 1 A g-1 current density, the specific capacity is 585.45 mA h g-1 after 400 cycles, and the minimum capacity attenuation per cycle is only 0.1076 mA h g-1 (0.0172% of the original capacity), which indicates excellent energy storage capacity and cycle stability. In summary, this research contributes to the development of advanced anode materials for next-generation energy storage systems, marking a stride toward sustainable energy solutions.

Perspectives Toward Damage-Tolerant Nanostructure Ceramics.

Advanced ceramic materials and devices call for better reliability and damage tolerance. In addition to their strong bonding nature, there are examples demonstrating superior mechanical properties of nanostructure ceramics, such as damage-tolerant ceramic aerogels that can withstand high deformation without cracking and local plasticity in dense nanocrystalline ceramics. The recent progresses shall be reviewed in this perspective article. Three topics including highly elastic nano-fibrous ceramic aerogels, load-bearing nanoceramics with improved mechanical properties, and implementing machine learning-assisted simulations toolbox in understanding the relationship among structure, deformation mechanisms, and microstructure-properties shall be discussed. It is hoped that the perspectives present here can help the discovery, synthesis, and processing of future structural ceramic materials that are insensitive to processing flaws and local damages in service.

How do different intraoral scanners and milling machines affect the fit and fatigue behavior of lithium disilicate and resin composite endocrowns?

The aim of this in vitro study was to evaluate the effect of the combinations of two different intraoral scanners (IOS), two milling machines, and two restorative materials on the marginal/internal fit and fatigue behavior of endocrowns produced by CAD-CAM. Eight groups (n= 10) were considered through the combination of TRIOS 3 (TR) or Primescan (PS) IOS; 4-axes (CR; CEREC MC XL) or 5-axes (PM; PrograMill PM7) milling machines; and lithium disilicate (LD; IPS e.max CAD) or resin composite (RC; Tetric CAD) restorative materials. Specific surface treatments were applied to each material, and the bonding to its corresponding Endocrown-shaped fiberglass-reinforced epoxy resin preparations was performed (Variolink Esthetic DC). Computed microtomography (µCT) was performed to assess the marginal/internal fit, as well as a mechanical fatigue test (20 Hz, initial load = 100 N/5000 cycles; step-size = 50 N/10,000 cycles until a threshold of 1500 N, then, the step-size was increased if needed to 100 N/10,000 cycles until failure or a threshold of 2800 N) to evaluate the restorations long-term behavior. Complementary analysis of the fracture features and surface topography in scanning electron microscopy was performed. Three-way ANOVA and Kaplan-Meier test (α = 0.05) were performed for marginal/internal fit, and fatigue behavior data, respectively. PS scanner, CR milling machine, and RC endocrowns resulted in a better marginal fit compared to their counterparts. Still, the PM machine resulted in a better pulpal space fit compared to the CR milling machine. Regardless of the scanner and milling machine, RC endocrowns exhibited superior fatigue behavior than LD ones. LD endocrowns presented margin chipping regardless of the milling machine used. Despite minor differences in terms of fit, the 'IOS' and 'milling machine' factors did not impair the fatigue behavior of endocrowns. Resin-composite restorations resulted in a higher survival rate compared to glass-ceramic ones, independently of the digital devices used in the workflow.

Fast Solution Blow Spinning of Lotus-Leaf-Inspired SiO2 Nanofiber Sponge for High Efficiency Purification.

Massive production of SiO2 nanofibers with both high durability and exceptional performance remains a significant challenge. Herein, a novel approach was introduced to achieve the massive production of SiO2 nanofibers with lotus-leaf-inspired surfaces by combining solution blowing spinning (SBS) and the polymer-derived ceramics method. Based on the SBS technique, three types of precursor nanofiber products were fast spined with methyl silsesquioxane polymer and polymethyl hydrogen siloxane employed as Si sources. The flow rate of the SBS spined Si-based ceramic nanofibers was enhanced to 20 mL·h-1. Furthermore, through the integration of hydrophobic-oleophilic SiO2 nanoparticles into the precursor solution, SiO2 nanofibers with lotus-leaf nanoprotrusion surfaces were fabricated. Nanoparticle-decorated SiO2 fibers demonstrated excellent hydrophobicity (138.3°), compression resilience (∼60%), proficiency in organic pollutant adsorption, high-temperature resistance (∼1100 °C), and outstanding thermal insulation properties (thermal conductivity of 0.0165 W·(m·K)-1).

Influence of thermal aging on the marginal integrity of computer aided design/computer aided manufacturing fabricated crowns.

Background/purpose: The adaptation and marginal integrity of computer-aided designed and computer-aided manufactured (CAD/CAM) crowns after exposure to thermal aging need to be investigated. The present in-vitro study was designed to investigate the marginal integrity of CAD/CAM fabricated crowns cemented on extracted teeth after thermocycling aging. Materials and methods: Twenty-six newly extracted human premolars were prepared for full-coverage CAD/CAM crowns and were divided into two groups (leucite-reinforced glass-ceramics and lithium disilicate glass-ceramics). Both crowns' groups were cemented using dual curing resin cement. All specimen margins were measured for marginal integrity using an imaging system 24 h post cementation; then after 1, 3, and 5 estimated clinical years (10,000, 30,000, and 50,000 thermocycles). Two-way ANOVA analysis were used to determine whether the mean value difference is significantly different (ɑ = 0.05). Results: The average margin gaps recorded for leucite-reinforced glass-ceramic crowns were: 82.61 µm initial, and 91.02 µm after 5 estimated clinical year). For the lithium disilicate glass-ceramic crowns, the average margin gaps recorded were: 100.01 µm initial, and 120.21 µm after 5 estimated clinical year. During all measuring intervals, the leucite-reinforced glass-ceramic crown group had a lower marginal discrepancy. No statistically significant difference between the two groups was recorded. Conclusion: After being subjected to thermocycling, both CAD/CAM ceramic crowns, exhibited an increase in their marginal discrepancy; the difference was within the accepted clinical range.

Temperature imaging inside fluid devices using a ratiometric near infrared (NIR-II/III) fluorescent Y2O3: Nd3+, Yb3+, Er3+ nanothermometer.

Luminescence thermometry is a non-contact method that can measure surface temperatures and the temperature of the area where the fluorescent probe is located, allowing temperature distribution visualizations with a camera. Ratiometric fluorescence thermometry, which uses the intensity ratio of fluorescence peaks at two wavelengths with different fluorescence intensity dependencies, is an excellent method for visualizing temperature distributions independent of the fluorophore spatial concentration, excitation light intensity and absolute fluorescence intensity. Herein, Nd3+/Yb3+/Er3+-doped Y2O3 nanomaterials with a diameter of 200 nm were prepared as phosphors for temperature distribution measurement of fluids at different temperatures. The advantages of this designed fluorescent material include non-aggregation in water and the fact that its near-infrared (NIR) fluorescence excitation (808 nm) is not absorbed by water, thereby minimizing sample heating upon irradiation. Under optical excitation at 808 nm, the ratio of the fluorescence intensities of Yb3+ (IYb; 975 nm) and Er3+ (IEr; 1550 nm), which exhibited different temperature responses, indicated the temperature distribution inside the fluid device. Thus, this technique using Nd3+/Yb3+/Er3+-doped Y2O3 is expected to be applied for temperature distribution mapping analysis inside fluidic devices as a ratiometric NIR fluorescence thermometer, which is unaffected by laser-induced heating.

Fabrication of Porous Anorthite Ceramic Insulation Using Solid Wastes.

Porous anorthite (CaAl2Si2O8) ceramics, suitable for thermal insulation in buildings, were obtained using waste seashells as a source of CaO, kaolin as a source of Al2O3 and SiO2 and banana peel as a pore former. Changing the volume of banana peel as well as the processing temperature was found to be an effective approach to control the thermo-mechanical properties of the obtained anorthite ceramics. The sintering of powder compacts containing up to 30 wt% banana peel at temperatures ranging from 1100 to 1200 °C resulted in anorthite ceramics possessing up to 45% open porosity, a compressive strength between 13 and 92 MPa, a bulk density between 1.87 and 2.62 g/cm3 and thermal conductivity between 0.097 and 3.5 W/mK. It was shown that waste materials such as seashells and banana peel can be used to obtain cost-effective thermal insulation in buildings.

Achieving High-Temperature Stable Structural Color through Nanostructuring in Polymer-Derived Ceramics.

Structural colors offer a myriad of advantages over conventional pigment-based colors, which often rely on toxic chemical substances that are prone to UV degradation. To take advantage of these benefits in demanding environments, there is growing interest in producing structural colors from ceramics. Polymer-derived ceramics (PDCs) emerge as a compelling choice, presenting two distinct advantages: their enhanced shape ability in their polymeric state associated with impressive temperature resistance once converted to ceramics. This study pioneers the fabrication of noniridescent structural colors from silicon oxycarbide (SiOC) PDC, enabled by the nanostructuring of an inverse photonic glass within the PDC material. This design, a functionally graded material with an inverse photonic glass (FGM-PhG) structure, leverages the innate light-absorbing properties of SiOC, yielding a vivid structural color that maintains its saturation even in white surroundings. This study elucidates the process-structure-properties relationship for the obtained structural colors by investigating each layer of the functionally graded material (FGM) in a stepwise coating deposition process. To further emphasize the exceptional processing flexibility of PDCs, the three-step process is later transferred to an additive manufacturing approach. Finally, the FGM-PhG structural colors are demonstrated to have remarkable thermal stability up to 1000 °C for 100 h, possibly making them the most thermally stable ceramic structural colors to date.

Advanced Ceramics with Dual Functions of Healing and Decomposition.

This study developed advanced ceramic materials with both healing and decomposition functions using a metastable product generated under superheated steam. The developed composite material comprises ZrC particles dispersed in a yttria-stabilized zirconia (YSZ) matrix. After introducing a surface crack of approximately 120 µm on the composite specimen, it showed a complete strength recovery rate after one hour of heat treatment under superheated steam at 400 °C, while it exhibited a decomposition behavior after one hour of heat treatment in air at 400 °C. The XRD analysis of the heat-treated specimens showed that the final product was monoclinic ZrO2 under both steam and air conditions. In other words, full strength recovery in superheated steam was achieved by a chain reaction involving metastable intermediate products derived from H2O, unlike the reaction in air.

Fabrication of Layered SiC/C/Si/MeSi2/Me Ceramic-Metal Composites via Liquid Silicon Infiltration of Metal-Carbon Matrices.

The growing demand for composite materials capable of enduring prolonged loads in high-temperature and aggressive environments presents pressing challenges for materials scientists. Ceramic materials composed of silicon carbide largely possess high mechanical strength at a relatively low density, even at elevated temperatures. However, they are inherently brittle in nature, leading to concerns about their ability to fracture. The primary objective of this study was to develop a novel technique for fabricating layered composite materials by incorporating SiC-based ceramics, refractory metals, and their silicides as integral constituents. These layered composites were produced through the liquid-phase siliconization method applied to metal-carbon blanks. Analysis of the microstructure of the resultant materials revealed that when a metal element interacts with molten silicon, it leads to the formation of a layer of metal silicide on the metal's surface. Furthermore, three-point bending tests exhibited an enhancement in the bending strength of the layered composite in comparison to the base silicon carbide ceramics. Additionally, the samples demonstrated a quasi-plastic nature during the process of destruction.

Boosted Second Harmonic Generation and Cascaded Sum Frequency Generation from a Surface Crystallized Glass Ceramic Microcavity.

The development of novel materials and structures for efficient second-order nonlinear micro/nano devices remains a significant challenge. In this study, the remarkable enhancement of second-harmonic generation (SHG) and cascaded sum frequency generation in whispering gallery mode microspheres made of surface-crystallized glass with a 6-µm Ba2TiSi2O8 crystal layer are demonstrated. Attributed to the core-shell design, the Ba2TiSi2O8 located on the surface can be efficiently coupled with whispering gallery modes, resulting in a highly efficient micron-scale cavity-enhanced second-order optical nonlinearity. Greatly enhanced SHG of the microcavity is observed, which is up to 80 times stronger than that of a non-resonant sample. Furthermore, owing to the wavelength non-selectivity of random quasi-phase matching, ultra-wideband SHG with a strong response ranging from 860 to 1600 nm and high-contrast polarization characteristics is demonstrated. The glass-ceramic-based microsphere cavity also boosts the cascading optical nonlinearity, manifested by a two-magnitude enhancement of cascaded sum frequency generation. This work delineates an efficient strategy for boosting nonlinear optical response in glass ceramics, which will open up new opportunities for applications in photonics and optical communications.

Effect of acidic environment on color and translucency of different indirect restorative materials.

PURPOSE: The aim of the current study was to evaluate the effect of simulated gastric acid on the color and translucency of different indirect restorative materials. MATERIALS AND METHODS: A total of 36 disc-shaped samples were cut by using an isomet saw and divided into four equal groups (n = 9) according to the material type: Group Z: translucent zirconia (Ceramill® Zolid ht.+ preshade, Amann Girrbach, Koblach, Austria); Group E: lithium disilicate (IPS e.max CAD, Ivoclar Vivadent AG, Schaan, Liechtenstein); Group C: resin nanoceramic (Cerasmart, GC, Tokyo, Japan); Group P: polyether ether ketone (PEEK) (Bettin Zirconia Dentale Italy) veneered with indirect high impact polymer composite (HIPC) (breCAM HIPC, Bredent GmbH & Co. KG, Germany). The samples were immersed in simulated gastric acid (HCl, pH 1.2) for 96 hours at 37 °C in an incubator. The color change (ΔE00) and translucency (RTP00) were measured every 9.6 hours (one-year clinical simulation) of immersion in simulated gastric acid. RESULTS: For color change (∆E00) and translucency (RTP00) among the tested materials, there was a highly statistically significant difference (P < 0.001) after every year of follow-up. The color change in both Z and G groups was the lowest after 1 year of acid immersion, followed by that in group H, and the highest change in color was recorded in group P. CONCLUSION: High translucent zirconia is recommended in patients who are concerned about esthetic, especially with acidic oral environment.

Methodological approaches in graded dental ceramics.

BACKGROUND: Functionally graded materials (FGM) with indistinct boundaries potentially eliminate the damaging stresses occurring at the interfaces. FGM applications in dental ceramics have enhanced their fatigue resistance and interfacial toughness. OBJECTIVES: This scoping review aims to map graded designs in dental ceramics, distinguish their methodological approaches with their material characteristics and properties, and understand the factors affecting the outcomes of each of the graded approaches. METHODS: A systematic electronic search was performed with the databases MEDLINE (PubMed), Scopus, Cochrane Library, EBSCO, and Google Scholar along with a manual search. RESULTS: About 2675 articles were initially found from all the searches with no date restriction till July 2023. After rejecting duplicates and based on exclusion criteria, about 52 articles were included. SIGNIFICANCE: Methodological approaches in grading such as glass-infiltration and silica-infiltration have been investigated on pre-sintered zirconia. The type of infiltration and the method of infiltrate application significantly influenced the phase transformation of zirconia, its microstructure, surface hardness, fracture toughness, flexural strength, wear, and fatigue strength of graded dental zirconia. Interlayers were accommodated between metal-ceramic and veneer-core all-ceramic layers. Fractions of zirconia-porcelain and alumina-porcelain showed high bending strength and better stress distribution. The results of finite element analysis studies predicted that using 10-layered graded layers reduced the stresses at the crown-cement-dentin interface.

Dental ceramic damage associated with incorrect laboratory procedures.

Ceramic is a commonly used material in dentistry for reconstructing missing teeth or their tissues due to its biocompatibility, durability and excellent esthetic properties. Despite these advantages, the ceramic restoration damage remains a significant clinical problem. Its causes can be divided into clinical and laboratory factors. The most known include uneven occlusion, improper preparation, trauma, or parafunctions. This study focuses on characterizing less known laboratory causes of ceramic restoration damage. We reviewed the current literature available in the PubMed and Scopus databases. On the basis of 63 selected studies, 3 basic causes of damage were identified: excessive stresses between the framework and ceramic veneering, poor quality of the connection between the facing layer and the substructure, and defects resulting from the nature of the ceramic material such as defects in the ceramic layer, brittleness and lack of flexibility. The stages of the manufacturing process of various permanent ceramic restorations were presented. By controlling these procedures, we can eliminate the errors, resulting in long-term effective functioning of the ceramic restorations.

Biosafety and chemical solubility studies of multiscale crystal-reinforced lithium disilicate glass-ceramics.

Lithium disilicate (Li2 Si2 O5 ) glass-ceramics are currently a more widely used all-ceramic restorative material due to their good mechanical properties and excellent aesthetic properties. However, they have a series of problems such as high brittleness and low fracture toughness, which has become the main bottleneck restricting its development. Therefore, in order to compensate for these shortcomings, we propose to prepare a reinforced glass-ceramics with better mechanical properties and to test the biosafety and chemical solubility of the material. Li2 Si2 O5 whiskers were synthesized by a one-step hydrothermal method, and multi-scale crystal-enhanced Li2 Si2 O5 glass-ceramics were prepared by reaction sintering. The biosafety of multi-scale crystal-reinforced Li2 Si2 O5 glass-ceramics was investigated by in vitro cytotoxicity test, rabbit pyrogen test, mice bone marrow micronucleus test, skin sensitization test, sub-chronic systemic toxicity test, and chronic systemic toxicity test. Additionally, the chemical solubility of multi-scale crystal-reinforced Li2 Si2 O5 glass-ceramics was investigated. The test results showed that the material was non-cytotoxic, non-thermogenic, non-mutagenic, non-sensitizing, and non-systemic. The chemical solubility, determined to be 377 ± 245 µg/cm2 , complied with the ISO 6872 standard for the maximum solubility of ceramic materials. Multi-scale crystal-reinforced Li2 Si2 O5 glass-ceramics' biosafety and chemical solubility met current normative criteria, and they can move on to mechanical property measurements (such as flexural strength test, fatigue life test, friction and wear property study, etc.) and bonding property optimization, which shows promise for future clinical applications.

Effect of 4-META on microtensile bond strength of cements to ceramics.

Background: This study assessed the effect of different concentrations of 4-methacryloyloxyethy trimellitate anhydride (4-META) added to silane on microtensile bond strength (µTBS) of light-cure and dual-cure resin cement to hybrid and zirconia-reinforced lithium silicate ceramics. Materials and Methods: This in vitro, experimental study was conducted on 32 Celtra Duo and 32 VITA Enamic ceramics bonded to Allcem Veneer light-cure and Allcem dual-cure resin cements using silane impregnated with 4-META in 0%, 2.5%, 5%, and 10 wt% concentrations in 16 groups (n = 4). The µTBS of specimens was measured by a universal testing machine and analyzed by the Kruskal-Wallis and Mann-Whitney tests, and the mode of failure was determined under a stereomicroscope and analyzed by the Chi-square test (alpha = 0.05). Results: The lowest mean µTBS was recorded in the Enamic ceramic group with 4-META (0%) bonded to dual-cure cement (14.26 MPa), and the highest mean µTBS was recorded in Enamic ceramic with 4-META (10%) bonded to light-cure cement (18.59 MPa) (P < 0.001). The µTBS of Celtra Duo was significantly higher than that of Enamic in bonding to light-cure cement using 4-META (2.5%) (P = 0.003). All failures (100%) were adhesive in most groups. The frequency of adhesive failure was the lowest (90%) in Celtra Duo bonded to dual-cure cement with 4-META (5%). Conclusion: According to the results of this pilot study, the addition of 4-META (10%) to silane caused a significant improvement in µTBS to light-cure cement. The addition of 4-META in all concentrations significantly improved the µTBS to Enamic ceramic in the use of dual-cure cement; however, it had no significant effect on µTBS of Celtra Duo. Nonetheless, the results should be interpreted with caution due to the relatively small sample size.

Monolithic hybrid abutment crowns: Influence of crown height, crown morphology and material on the implant-abutment complex.

PURPOSE: This in vitro study investigated the influence of material selection, crown morphology, and vertical crown height on the biomechanical behavior of monolithic hybrid abutment crowns (HACs). METHODS: Ninety implants were embedded in accordance with ISO standard 14801; ninety HACs were mounted (N=90). Monolithic crowns with varying group-specific designs were luted using titanium bases. HACs were fabricated from monolithic lithium disilicate ceramic (LD) or zirconia-reinforced lithium silicate ceramic (ZLS). The crown morphology was either maxillary premolar (LD_PM, ZLS_PM) or molar (LD_MO). The three groups were further divided into three subgroups of ten specimens, each designed with a small (7.5 mm), middle (10.5 mm), and high (13.5 mm) configuration of crown heights (N=10). A load-to-failure test at 30° off-axis was conducted using a universal testing machine until failure. For statistical analysis, Kolmogorov-Smirnov and Mann-Whitney U tests were conducted (P < 0.05). RESULTS: All LD_MO groups presented the highest failure values (808.7 to 947.9 N), followed by the LD_PM (525.8 to 722.8 N) and ZLS_PM groups (312.6 to 478.8N). A comparison between LD and ZLS materials (P < 0.001) as well as the crown morphology (P < 0.001) showed significant differences in failure values. The values in the subgroups of ZLS_PM (low, middle, high) decreased as the crown height increased. The fracture modes showed no consistent patterns across the test groups. CONCLUSIONS: Material selection, crown morphology, and vertical crown height appear to be important factors that may influence the clinical failure values and patterns of HACs.